WEICON HB 300 Technisches Datenblattcnco_de_tds_weicon_hb_300.pdf
331.44 kB
2-component epoxy resin adhesive
1.0 kg tin Weicon Plastik-Stahl HB-300Item-no.: 1181063Supplier number: 10000099customs tariff number: 29109000EAN: 4024596003050
Quantity:
1 Piece
=
1 PackagingPackable
Item available in 1 variants:
Price and stock visible after login
Description
WEICON HB 300 is pasty, steel-filled and high-temperature-resistant up to +200°C (392°F) (up to 280°C/536°F for a short period of time). It is processed with a mixing ratio of 1:1. The epoxy resin system is also suitable for applications on vertical surfaces and can be used for the repair and bonding of cast and metal parts, for filling in blow holes, for repairing damage on containers, carriages and machine parts and for sealing pumps and pipes. The product can be used in mechanical and plant engineering, in equipment engineering, and in many other areas of industry.
Attributes
Adhesive strength|DIN EN ISO 4624
20.0 MPa
Aluminium sandblasted
8 N/mm²
Base
Epoxy
Bending strength |DIN EN ISO 178
42.0 MPa
Coating sequence time|(35 % of strength)
6 Hours
Colour
dark grey
Component temperature
>3 °C above dew point
Compressive strength|DIN EN ISO 604
100.0 MPa
Consistency
pasty
Construction material class|DIN 4102
B2
Consumption|layer thickness 1.0 mm
2.5 kg/m²
Density of hardener
2.5 g/cm³
Density of the mixture
2,5 g/cm³
Density resin
2.3 g/cm³
E-modulus (tensile)|DIN EN ISO 527-2
7000-7200 MPa
Elongation at break (tensile)|DIN EN ISO 527-2
0,7 %
End hardness|(100 % of strength)
24 Hours
Filling material
Steel
Hardness (Shore D)|DIN ISO 7619
85±3
Heat deflection temperature|DIN EN ISO 75-2 (*after tempering)
+100* °C
Magnetic
ja
Max. layer thickness | per work step
20.0 mm
Mechanically loadable after|(80 % of strength)
10 Hours
Mixing ratio by volume
100:90
Mixing ratio by weight
100:100
Processing temperature
+15 °C to +40 °C °C
Relative humidity
< 85 %
Sales bundle
Plastic box
Shrinkage
0,15 %
Stainless steel V2A sandblasted
15.0 MPa
Steel 1.0338 sandblasted
14.0 MPa
Temperature resistance
-35 °C to +200 °C briefly up to +280 °C
Tensile strength|DIN EN ISO 527-2
50.0 MPa
Tg after curing at RT|(DSC)
~ +57 °C
Thermal capacity|DIN EN ISO 22007-4
0.63 J/(g·K)
Thermal conductivity|DIN EN ISO 22007-4
0.5 W/m·K
Through resistance|DIN EN 62631-3-1
1,5·10¹³ Ω·m
Topfzeit|bei 20 °C, 500 g Ansatz
30 Min.
Viscosity of the mixture|at +25 °C
1.700.000 mPa·s