2-component epoxy resin adhesive

24 ml double syringe Weicon Aluminium Minute Adhesive

Item-no.: 1414577Supplier number: 10051229customs tariff number: 35061000EAN: 4024596061050

PU (Packaging): 12 PieceQuantity:  1 PiecePackable

Description

WEICON Aluminium Minute Adhesive is an odourless, two-component epoxy adhesive filled with aluminium. It cures fast at room temperature and practically without shrinkage. After curing, the adhesive can be machined (filing, drilling, milling). Aluminium Minute Adhesive is gap-filling and non-dripping (thixotropic) and shows very high tensile, impact and peel strength. The adhesive is particularly suitable for bonding aluminium and other light metals. It can be used for filling cracks and holes on aluminium housings, for example, and for repairing light alloy wheels. In order to achieve optimal adhesion, the bonding surfaces should be dry and free from grease or dirt. Scraping or sanding the surfaces before cleaning additionally improves adhesion.

Attributes

Aluminium sandblasted

19 N/mm²

Base

Epoxy resin, highly filled

Bauteiltemperatur

>3°C über Taupunkt

Bending strength |DIN EN ISO 178

58.0 MPa

Breite

40.0

Colour

aluminium

Compressive strength|DIN EN ISO 604

8.0 MPa

Consistency

pasty, gap-filling

Construction material class|DIN 4102

Curing temperature

+6 °C - +40 °C

Density of the mixture

1,23 g/cm³

Dielectric strength|DIN EN 60243-1 (20°C)

16 kV/mm

E-modulus (tensile)|DIN EN ISO 527-2

4.000 - 4.500 MPa

Edelstahl V2A sandgestrahlt

19.0 N/mm²

End hardness|(100 % of strength)

24 Hours

Füllstoff

gefüllt

Gap bridging up to max.

4 mm

Hardness (Shore D)|DIN ISO 7619

Lieferumfang

Klebstoff

Manual strength|(35 % of strength)

25 Min.

Mechanically loadable after|(50 % of strength)

2 Hours

Mischungsverhältnis nach Volumen

1:1

Mixing ratio by weight

1:1

PVC-hard roughened

11.0 N/mm²

Processing temperature

+10 °C to +30 °C °C

Sales bundle

Cartridge

Shrinkage

0,3 %

Steel 1.0338 sandblasted

20.0 N/mm²

Temperature resistance

-50 °C to + 120 °C short term up to +150 °C

Tensile strength|DIN EN ISO 527-2

34.0 MPa

Topfzeit|bei 20 °C, 10 ml Ansatz

4-5 Min.

Viscosity of the mixture|at +20 °C

125.000 mPa·s

magnetisch

nein

relative Luftfeuchtigkeit

max. 85%

Downloads

Aluminium-Minutenkleber Technisches Datenblattcnco_de_tds_aluminium-minutenkleber.pdf
244.83 kB

Sicherheitsdatenblattcnco_sds_de_de_105521_aluminium-minutenkleber_harz.pdf
280.8 kB

Sicherheitsdatenblattcnco_sds_de_de_105522_aluminium-minutenkleber_haerter.pdf
261.14 kB